摘要: |
为了制备催化性能优良的负载型TiO2光催化剂,以沸石为载体,采用正交设计法优化了浸渍法制TiO2/沸石光催化剂的工艺参数,以其对硫酸铵溶液中的氨氮降解率为考察指标,对其催化性能进行了研究。结果表明,制备TiO2/沸石光催化剂的最佳工艺条件为:m(TiO2)∶m(沸石)∶m(硅酸钠)=0.7∶10∶15,老化时间24 h,焙烧温度为400 ℃,焙烧时间1h。TiO2/沸石光催化剂最佳投放量为1.5 g/L,在紫外光照射下反应4 h,对废水的氨氮去除率可达98.92%。可见,采用优化浸渍法制备的TiO2/沸石光催化剂的光催化性能优良。 |
关键词: 沸石 光催化剂 氨氮去除率 |
DOI: |
分类号: |
基金项目: |
|
Preparation and photocatalytic behavior of TiO2-coated zeolite photocatalyst |
|
Abstract: |
Titanium dioxide-coated zeolite was prepared by the method of impregnation in order to find TiO2 photocatalyst with good catalytic properties.The major influential factors were optimized.This paper selected the degradation of N-NH3 as characterization of photocatalytic perfomance.The following results were obtained:the m(TiO2)∶m(zeolite)∶m(Na2SiO3) mass ratio was 0.7∶10∶15,the calcinations temperature was about 400 ℃,the calcinations time was 1 h,and the aging time was 24 h.Under UV radiation,98.92% of N-NH3 was photo-catalytically degraded by TiO2 coated zeolite photocatalyst for 4 h,and the optimum weight of TiO2 coated zeolite photocatalyst was 1.5 g/L TiO2 coated zeolite photocatalyst.The results indicated that the TiO2/zeolite prepared by the method of impregnation had a good performance of photodegradation. |
Key words: zeolite TiO2 photocatalyst degradation of N-NH3-containing wastewater |